1. Odcedzić rozwiązanie odpuszczania sprężyn
The strain spring tempering solution refers to applying a tensile stress equivalent to 20 percent to 40 percent of the tensile strength at both ends of the tempered steel wire. The steel wire causes a small amount of strain under the tension effect, and the dislocation line moves. At this time, the interstitial solute atoms ( C and N atoms) diffuse to the vicinity of the dislocation line by means of temperature, "pinning" the moving dislocation. The carbides dispersed and precipitated during the whole tempering process showed a large number of pinning points, which made the dislocation "pinning" more thorough and sufficient, improved the plastic deformation resistance of the steel wire, and improved the elastic reduction characteristics of the steel wire.
2. Rozwiązanie ogrzewania sprężyn indukcyjnych
Sprężyna indukcyjna ma dużą prędkość nagrzewania, powierzchnia drutu stalowego jest lekko utleniona, odwęglenie nie jest łatwe, a ziarna są również rafinowane. Wytrzymałość i twardość oraz charakterystyka redukcji sprężystości są bardzo dobre, a ciężar można zmniejszyć o 10 do 20 procent pod warunkiem, że różne wskaźniki sprężyny zostaną utrzymane na pierwotnym poziomie. W przypadku stali sprężynowych zawierających wanad i niob tylko wyższą temperaturę austenityzowania można zastosować do pełnego rozpuszczenia wanadu i niobu oraz uzyskać rzeczywisty efekt odpuszczania wtórnego hartowania. W zwykłym standardzie ogrzewania temperatura austenityzowania jest zbyt wysoka, ziarna drutu stalowego są gruboziarniste, a utlenianie i odwęglanie powierzchni również gwałtownie wzrasta, co poważnie wpływa na trwałość zmęczeniową. Podczas nagrzewania indukcyjnego do 800 1000 stopni drut stalowy nie jest podatny na odwęglanie, silne utlenianie i gruboziarnistość. Dlatego ogrzewanie indukcyjne może w pełni wykorzystać zalety stali sprężynowej zawierającej wanad i niob.